Ashley Polymers Ashlene® 830L-25G Nylon 6, 25% Glass Reinforced
Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, 30% Glass Fiber Filled
Ashley Polymers
产品说明:
A 25% glass fiber reinforced Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type material.
Data provided by the manufacturer
Ashley Polymers Ashlene® 830L-25G Nylon 6, 25% Glass Reinforced 物性表
| 物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 密度 |
1.31 g/cc |
0.0473 lb/in3 |
ASTM D792 |
| 吸水率 |
1.1 % |
1.1 % |
ASTM D570 |
| 线性成型收缩率 |
0.0030 cm/cm |
0.0030 in/in |
ASTM D955 |
| 机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 洛氏硬度（R 级） |
119 |
119 |
ASTM D785 |
| 抗张强度(屈服) |
159 MPa |
23100 psi |
ASTM D638 |
| 伸长率 (断裂) |
3.0 % |
3.0 % |
ASTM D638 |
| 屈服伸长率 |
2.0 % |
2.0 % |
ASTM D638 |
| 弯曲强度 |
193 MPa |
28000 psi |
ASTM D790 |
| 弯曲模量 |
7.60 GPa |
1100 ksi |
ASTM D790 |
| 悬壁梁缺口冲击强度 |
0.960 J/cm |
1.80 ft-lb/in |
ASTM D256 |
| 热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 熔融温度 |
216 °C |
421 °F |
ASTM D3418 |
| 载荷下热变形温度(0.46 MPa) |
213 °C |
415 °F |
ASTM D648 |
| 载荷下热变形温度(1.8 MPa) |
208 °C |
406 °F |
AST |