LEXAN 美国沙伯基础创新 PC 244RF 物性表
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
ASTM D792 |
| -- |
1.20 |
g/cm3 |
ASTM D792 |
| -- |
1.19 |
g/cm3 |
ASTM D792 |
| 特定体积 |
0.830 |
cm3/g |
ASTM D792 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) |
11 |
g/10 min |
ASTM D1238 |
| 收缩率 - 流动(3.20 mm) |
0.50 到 0.70 |
% |
内部方法 |
| 吸水率 |
|
|
ASTM D570 |
| 24 hr |
0.15 |
% |
ASTM D570 |
| 平衡, 23°C |
0.35 |
% |
ASTM D570 |
| 平衡, 100°C |
0.58 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 |
|
|
ASTM D785 |
| M 级 |
70 |
|
ASTM D785 |
| R 级 |
118 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度1 |
|
|
ASTM D638 |
| 屈服 |
62.0 |
MPa |
ASTM D638 |
| 断裂 |
68.0 |
MPa |
ASTM D638 |
| 伸长率2 |
|
|
ASTM D638 |
| 屈服 |
7.0 |
% |
ASTM D638 |
| 断裂 |
130 |
% |
ASTM D638 |
| 弯曲模量3(50.0 mm 跨距) |
2340 |
MPa |
ASTM D790 |
| 弯曲强度4(屈服, 50.0 mm 跨距) |
96.0 |
MPa |
ASTM D790 |
| 泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮) |
10.0 |
mg |
ASTM D1044 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度(23°C) |
800 |
J/m |
ASTM D256 |
| 无缺口悬臂梁冲击(23°C) |
3200 |
J/m |
ASTM D4812 |
| 落锤冲击(23°C) |
169 |
J |
ASTM D3029 |
| 拉伸冲击强度5 |
577 |
kJ/m2 |
ASTM D1822 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm |
137 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm |
132 |
°C |
ASTM D648 |
| 维卡软化温度 |
154 |
°C |
ASTM D15256 |
| 线形热膨胀系数 - 流动(-40 到 95°C) |
6.8E-5 |
cm/cm/°C |
ASTM E831 |
| 比热 |
1250 |
J/kg/°C |
ASTM C351 |
| 导热系数 |
0.27 |
W/m/K |
ASTM C177 |
| RTI Elec |
130 |
°C |
UL 746 |
| RTI Imp |
130 |
°C |
UL 746 |
| RTI |
130 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 体积电阻率 |
1.0E 17 |
ohms·cm |
ASTM D257 |
| 介电强度(3.20 mm, in Air) |
15 |
kV/mm |
ASTM D149 |
| 介电常数 |
|
|
ASTM D150 |
| 50 Hz |
3.17 |
|
ASTM D150 |
| 60 Hz |
3.17 |
|
ASTM D150 |
| 1 MHz |
2.96 |
|
ASTM D150 |
| 耗散因数 |
|
|
ASTM D150 |
| 50 Hz |
9.0E-4 |
|
ASTM D150 |
| 60 Hz |
9.0E-4 |
|
ASTM D150 |
| 1 MHz |
0.010 |
|
ASTM D150 |
| 相比耐漏电起痕指数(CTI) |
PLC 2 |
|
UL 746 |
| 高电弧燃烧指数(HAI) |
PLC 1 |
|
UL 746 |
| 高电压电弧起痕速率 (HVTR) |
PLC 2 |
|
UL 746 |
| 热丝引燃 (HWI) |
PLC 2 |
|
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级(1.5 mm) |
V-2 |
|
UL 94 |
| 灼热丝易燃指数(1.0 mm) |
850 |
°C |
IEC 60695-2-12 |
| 热灯丝点火温度(1.0 mm) |
875 |
°C |
IEC 60695-2-13 |
| 极限氧指数 |
25 |
% |
ASTM D2863 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 折射率 |
1.586 |
|
ASTM D542 |
| 透射率(2540 μm) |
88.0 |
% |
ASTM D1003 |
| 雾度(2540 μm) |
1.0 |
% |
ASTM D1003 |