Solvay TECHNYL A 208F PA66, DRY

Technyl®一208F PA66、干
类别：聚合物；热塑性；尼龙；尼龙66
材料说明：说明：非增强尼龙PA66、热稳定、高流动性、快速循环级，注塑成型。
可在：欧洲
产品应用：Technyl 208F提供了三个主要的优势：优良的填充质量，长期良好的热性能，V2额定在0.4毫米。根据UL94。特别适用于要求具有良好耐热性的薄壁型材的长零件的成型：电缆扎带和紧固件和连接器。本产品可在天然和黑色。
罗地亚罗地亚提供的信息，已收购Solvay。

Solvay TECHNYL A 208F PA66, DRY美国苏威

Physical Properties Metric English Comments Density  1.14 g/cc 0.0412 lb/in3 ISO 1183/A Water Absorption  1.2 % @Temperature 23.0 °C, Time 86400 sec 1.2 % @Temperature 73.4 °F, Time 24.0 hour ISO 62 Linear Mold Shrinkage  0.010 cm/cm 0.010 in/in Isotropy Linear Mold Shrinkage, Flow  0.020 cm/cm 0.020 in/in Linear Mold Shrinkage, Transverse  0.020 cm/cm 0.020 in/in   Mechanical Properties Metric English Comments Tensile Strength at Break  60.0 MPa 8700 psi ISO 527 Type 1A Tensile Strength, Yield  85.0 MPa 12300 psi ISO 527 type 1 A Elongation at Yield  7.0 % 7.0 % ISO 527 type 1 A Tensile Modulus  3.20 GPa 464 ksi ISO 527 Type 1A Flexural Modulus  2.90 GPa 421 ksi ISO 178 Izod Impact, Notched (ISO)  4.50 kJ/m2 2.14 ft-lb/in2 ISO 180/1A Charpy Impact Unnotched  NB NB ISO 179/1eU Charpy Impact, Notched  0.450 J/cm2 2.14 ft-lb/in2 ISO 179/1eA   Electrical Properties Metric English Comments Volume Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm IEC 60093 Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 60093 Dielectric Constant  2.9 2.9 IEC 60250 Dielectric Strength  27.0 kV/mm 686 kV/in IEC 60243 Dissipation Factor  0.030 0.030 IEC 60250 Comparative Tracking Index  375 V 375 V Solution B; IEC 60112   475 V 475 V Solution A; IEC 60112   Thermal Properties Metric English Comments CTE, linear  70.0 μm/m-°C @Temperature 23.0 - 85.0 °C 38.9 μin/in-°F @Temperature 73.4 - 185 °F ISO 11359 Melting Point  263 °C 505 °F ISO 11357 Deflection Temperature at 1.8 MPa (264 psi)  75.0 °C 167 °F ISO 75/Af Flammability, UL94   V-2 @Thickness 0.380 mm V-2 @Thickness 0.0150 in ISO 1210   V-2 @Thickness 0.800 mm V-2 @Thickness 0.0315 in ISO 1210   V-2 @Thickness 1.60 mm V-2 @Thickness 0.0630 in ISO 1210 Oxygen Index  26 % 26 % ISO 4589 Glow Wire Test   650 °C @Thickness 1.60 mm 1200 °F @Thickness 0.0630 in Ignition Temperature; ISO 60695-2-13   850 °C @Thickness 1.60 mm 1560 °F @Thickness 0.0630 in ISO 60695-2-12   Processing Properties Metric English Comments Feed Temperature  265 - 275 °C 509 - 527 °F Mold Temperature  60.0 - 80.0 °C 140 - 176 °F Drying Temperature  80.0 °C 176 °F Moisture Content  <= 0.20 % <= 0.20 %   Descriptive Properties Compression Zone 270-280°C Mixing Zone 280-285°C

  Solvay TECHNYL® eXten D 458P PA6.10, Conditioned
  Solvay TECHNYL® 1011R PA6, DRY
  Solvay TECHNYL® 1011R PA6, Conditioned
  Solvay TECHNYL® 1015CR PA6, DRY
  Solvay TECHNYL® 1015CR PA6, Conditioned
  Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, DRY
  Solvay TECHNYL® 1021ST PA6, DRY
  Solvay TECHNYL® 1021ST PA6, DRY
  Solvay TECHNYL® 1021ST PA6, Conditioned
  Solvay TECHNYL® 2210HS PA66, DRY
  Solvay TECHNYL® 2210HS PA66, Conditioned
  Solvay TECHNYL® 2411GF6 PA66, 30% glass fiber, DRY
  Solvay TECHNYL® 2411GF6 PA66, 30% glass fiber, Conditioned
  Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, DRY
  Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, Conditioned
  Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY
  Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, Conditioned
  Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY
  Solvay TECHNYL® 2417IG PA66, 20% glass fiber, DRY
  Solvay TECHNYL® 2710IR PA66, DRY
  Solvay TECHNYL® 2710IR PA66, Conditioned
  Solvay TECHNYL® 27010ST PA66, DRY
  Solvay TECHNYL® 27010ST PA66, Conditioned
  Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY
  Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0
  Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, DRY
  Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, Conditioned
  Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, DRY
  Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned
  Solvay TECHNYL® A 205F PA66, DRY
  Solvay TECHNYL® A 205F PA66, Conditioned
  Solvay TECHNYL® A 208F PA66, DRY
  Solvay TECHNYL® A 208F PA66, Conditioned
  Solvay TECHNYL® A 208KBK-10N-L PA66, DRY
  Solvay TECHNYL® A 208KBK-10N-L PA66, Conditioned
  Solvay TECHNYL® A 216 NATURAL FA PA66, DRY
  Solvay TECHNYL® A 216 NATURAL FA PA66, Conditioned
  Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY
  Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, Conditioned
  Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, DRY
  Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, Conditioned
  Solvay TECHNYL® A 216 V15 Black 21N PA66, 15% glass fiber, DRY
  Solvay TECHNYL® A 216 V15 Black 21N PA66, 15% glass fiber, Conditioned



 

Solvay TECHNYL A 208F PA66, DRY 美国苏威

18.TECHNYL PA66 A 216 S40:30%玻璃珠填料.

特点  表面光洁度好 低翘曲 良好的压缩强度
   
外貌  黑色  本色 
 
处理方法  注塑成型

19.TECHNYL PA66 A 216 V10:10%玻璃纤维增强，注射成型。

添加剂  润滑剂 
 
特点  润滑 
 
用途  汽车应用 建材 电源/其它工具 
 
外貌  黑色 可选颜色 本色 
 
处理方法  注塑成型 

20.TECHNYL PA66 A 216 V15:15％的玻璃纤维增强，注射成型
 
添加剂  润滑剂 
 
特点  润滑 
 
用途  汽车应用 建材 电源/其它工具 
 
外貌  黑色 可选颜色 灰色 本色 
   
处理方法  注塑成型 

21.TECHNYL PA66 A 216 V20:20％的玻璃纤维增强，注射成型
 
添加剂  润滑剂 
 
特点  润滑 
 
用途  汽车应用 建材 电源/其它工具 
 
外貌  黑色 可选颜色 本色 
 
处理方法  注塑成型

22.TECHNYL PA66 A 216 V30:30％的玻璃纤维增强，注射成型

添加剂  润滑剂 
 
特点  润滑 
 
用途  汽车应用 建材 电源/其它工具 
 
外貌  黑色 可选颜色 本色 
 
处理方法  注塑成型 

23.TECHNYL PA66 A 216 V35:聚酰胺尼龙66，35％的玻璃纤维增强，注射成型
 
添加剂  润滑剂 
 
特点  润滑 
 
用途  汽车应用 建材 电源/其它工具 
 
外貌  黑色 可选颜色 本色 
 
处理方法  注塑成型 



Solvay TECHNYL A 208F PA66, DRY原厂原包，可提供原产地证明 、COA.COC.ROHS.MSDS.UL等资料。