Solvay TECHNYL A 205F PA66, DRY
Technyl®一205F PA66、干
类别：聚合物；热塑性；尼龙；尼龙66
材料说明：说明：TECHNYL®一205F是一个无筋尼龙66注塑成型。它可在自然颜色。
优点：该产品提供了两个主要优点：优良的填充质量和UL 94 V2在0.4毫米。它特别适用于薄壁型材长零件的成型。
可在：亚太，欧洲，拉丁美洲和美国北部
法规：等级的生产或进口欧洲符合指令453／2010／EC，修订REACH指令1907 / 2006 / EC，这种等级符合RoHS指令2002／95／EC。除非指定，这个等级是不适合于食品接触，医疗设备或玩具应用。
应用：电缆扎带，紧固件或连接器
罗地亚罗地亚提供的信息，已收购Solvay。
Solvay TECHNYL A 205F PA66, DRY美国苏威
| |
| Physical Properties |
Metric |
English |
Comments |
| Density |
1.14 g/cc |
0.0412 lb/in3 |
ISO 1183/A |
| Water Absorption |
1.2 %
@Temperature 23.0 °C,
Time 86400 sec |
1.2 %
@Temperature 73.4 °F,
Time 24.0 hour |
ISO 62 |
Viscosity  |
20 cP
@Shear Rate 10000 1/s,
Temperature 300 °C |
20 cP
@Shear Rate 10000 1/s,
Temperature 572 °F |
|
| |
21 cP
@Shear Rate 10000 1/s,
Temperature 290 °C |
21 cP
@Shear Rate 10000 1/s,
Temperature 554 °F |
|
| |
22 cP
@Shear Rate 10000 1/s,
Temperature 280 °C |
22 cP
@Shear Rate 10000 1/s,
Temperature 536 °F |
|
| |
50 cP
@Shear Rate 1000 1/s,
Temperature 300 °C |
50 cP
@Shear Rate 1000 1/s,
Temperature 572 °F |
|
| |
80 cP
@Shear Rate 1000 1/s,
Temperature 290 °C |
80 cP
@Shear Rate 1000 1/s,
Temperature 554 °F |
|
| |
90 cP
@Shear Rate 100 1/s,
Temperature 300 °C |
90 cP
@Shear Rate 100 1/s,
Temperature 572 °F |
|
| |
101 cP
@Shear Rate 1000 1/s,
Temperature 280 °C |
101 cP
@Shear Rate 1000 1/s,
Temperature 536 °F |
|
| |
120 cP
@Shear Rate 100 1/s,
Temperature 280 °C |
120 cP
@Shear Rate 100 1/s,
Temperature 536 °F |
|
| |
120 cP
@Shear Rate 100 1/s,
Temperature 290 °C |
120 cP
@Shear Rate 100 1/s,
Temperature 554 °F |
|
| Linear Mold Shrinkage |
0.010 cm/cm |
0.010 in/in |
Isotropy |
| Linear Mold Shrinkage, Flow |
0.019 cm/cm |
0.019 in/in |
|
| Linear Mold Shrinkage, Transverse |
0.019 cm/cm |
0.019 in/in |
|
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Tensile Strength at Break |
60.0 MPa |
8700 psi |
ISO 527 Type 1A |
| Tensile Stress |
15.0 MPa
@Strain 10.0 %,
Temperature 150 °C |
2180 psi
@Strain 10.0 %,
Temperature 302 °F |
|
| |
19.0 MPa
@Strain 10.0 %,
Temperature 120 °C |
2760 psi
@Strain 10.0 %,
Temperature 248 °F |
|
| |
21.0 MPa
@Strain 20.0 %,
Temperature 150 °C |
3050 psi
@Strain 20.0 %,
Temperature 302 °F |
|
| |
24.0 MPa
@Strain 30.0 %,
Temperature 150 °C |
3480 psi
@Strain 30.0 %,
Temperature 302 °F |
|
| |
25.0 MPa
@Strain 10.0 %,
Temperature 80.0 °C |
3630 psi
@Strain 10.0 %,
Temperature 176 °F |
|
| |
25.0 MPa
@Strain 20.0 %,
Temperature 120 °C |
3630 psi
@Strain 20.0 %,
Temperature 248 °F |
|
| |
30.0 MPa
@Strain 30.0 %,
Temperature 120 °C |
4350 psi
@Strain 30.0 %,
Temperature 248 °F |
|
| |
39.0 MPa
@Strain 20.0 %,
Temperature 80.0 °C |
5660 psi
@Strain 20.0 %,
Temperature 176 °F |
|
| |
42.0 MPa
@Strain 30.0 %,
Temperature 80.0 °C |
6090 psi
@Strain 30.0 %,
Temperature 176 °F |
|
| |
45.0 MPa
@Strain 40.0 %,
Temperature 80.0 °C |
6530 psi
@Strain 40.0 %,
Temperature 176 °F |
|
| |
70.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C |
10200 psi
@Strain 2.50 %,
Temperature 73.4 °F |
|
| Tensile Strength, Yield |
85.0 MPa |
12300 psi |
ISO 527 type 1 A |
| |
155 MPa |
22500 psi |
ASTM D638 |
| Elongation at Break |
25 % |
25 % |
ASTM D638 |
| |
50 % |
50 % |
ISO 527 Type 1A |
| Elongation at Yield |
4.0 % |
4.0 % |
ISO 527 type 1 A |
| Tensile Modulus |
3.20 GPa |
464 ksi |
ISO 527 Type 1A |
| Flexural Strength |
120 MPa |
17400 psi |
ISO 178 |
| |
125 MPa |
18100 psi |
ASTM D790 |
| Flexural Modulus |
3.00 GPa |
435 ksi |
ISO 178 |
| |
3.35 GPa |
486 ksi |
ASTM D790 |
| Izod Impact, Notched (ISO) |
5.00 kJ/m2 |
2.38 ft-lb/in2 |
ISO 180/1A |
| |
80.0 kJ/m2 |
38.1 ft-lb/in2 |
ISO 180/1A |
| Charpy Impact Unnotched |
NB |
NB |
ISO 179/1eU |
| Charpy Impact, Notched |
0.500 J/cm2 |
2.38 ft-lb/in2 |
ISO 179/1eA |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Volume Resistivity |
1.00e+15 ohm-cm |
1.00e+15 ohm-cm |
IEC 60093 |
| Surface Resistance |
5.00e+14 ohm |
5.00e+14 ohm |
IEC 60093 |
| Dielectric Constant |
2.9 |
2.9 |
IEC 60250 |
| Dielectric Strength |
27.0 kV/mm |
686 kV/in |
IEC 60243 |
| Dissipation Factor |
0.030 |
0.030 |
IEC 60250 |
| Comparative Tracking Index |
550 V |
550 V |
Solution B; IEC 60112 |
| |
600 V |
600 V |
Solution A; IEC 60112 |
| |
| Thermal Properties |
Metric |
English |
Comments |
| CTE, linear, Parallel to Flow |
70.0 μm/m-°C
@Temperature 23.0 - 85.0 °C |
38.9 μin/in-°F
@Temperature 73.4 - 185 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow |
7.00 μm/m-°C
@Temperature 23.0 - 85.0 °C |
3.89 μin/in-°F
@Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point |
262 °C |
504 °F |
ASTM D3418 |
| |
263 °C |
505 °F |
ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) |
80.0 °C |
176 °F |
ASTM D648 |
| Flammability, UL94 |
V-2
@Thickness 0.400 mm |
V-2
@Thickness 0.0157 in |
ISO 1210 |
| |
V-2
@Thickness 0.800 mm |
V-2
@Thickness 0.0315 in |
ISO 1210 |
| |
V-2
@Thickness 1.60 mm |
V-2
@Thickness 0.0630 in |
ISO 1210 |
| Oxygen Index |
29 % |
29 % |
ISO 4589 |
| Glow Wire Test |
850 °C |
1560 °F |
ISO 60695-2-12 |
| |
| Processing Properties |
Metric |
English |
Comments |
| Feed Temperature |
265 - 275 °C |
509 - 527 °F |
|
| Mold Temperature |
60.0 - 80.0 °C |
140 - 176 °F |
|
| Drying Temperature |
80.0 °C |
176 °F |
|
| Moisture Content |
<= 0.20 % |
<= 0.20 % |
|
| |
| Descriptive Properties |
| Compression Zone |
270-280°C |
|
| Mixing Zone |
280-290°C |
|
| |
|
Solvay TECHNYL® eXten D 458P PA6.10, Conditioned
Solvay TECHNYL® 1011R PA6, DRY
Solvay TECHNYL® 1011R PA6, Conditioned
Solvay TECHNYL® 1015CR PA6, DRY
Solvay TECHNYL® 1015CR PA6, Conditioned
Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, DRY
Solvay TECHNYL® 1021ST PA6, DRY
Solvay TECHNYL® 1021ST PA6, DRY
Solvay TECHNYL® 1021ST PA6, Conditioned
Solvay TECHNYL® 2210HS PA66, DRY
Solvay TECHNYL® 2210HS PA66, Conditioned
Solvay TECHNYL® 2411GF6 PA66, 30% glass fiber, DRY
Solvay TECHNYL® 2411GF6 PA66, 30% glass fiber, Conditioned
Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, DRY
Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, Conditioned
Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY
Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, Conditioned
Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY
Solvay TECHNYL® 2417IG PA66, 20% glass fiber, DRY
Solvay TECHNYL® 2710IR PA66, DRY
Solvay TECHNYL® 2710IR PA66, Conditioned
Solvay TECHNYL® 27010ST PA66, DRY
Solvay TECHNYL® 27010ST PA66, Conditioned
Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY
Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0
Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, Conditioned
Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, DRY
Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned
Solvay TECHNYL® A 205F PA66, DRY
Solvay TECHNYL® A 205F PA66, Conditioned
Solvay TECHNYL® A 208F PA66, DRY
Solvay TECHNYL® A 208F PA66, Conditioned
Solvay TECHNYL® A 208KBK-10N-L PA66, DRY
Solvay TECHNYL® A 208KBK-10N-L PA66, Conditioned
Solvay TECHNYL® A 216 NATURAL FA PA66, DRY
Solvay TECHNYL® A 216 NATURAL FA PA66, Conditioned
Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY
Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, Conditioned
Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, DRY
Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, Conditioned
Solvay TECHNYL® A 216 V15 Black 21N PA66, 15% glass fiber, DRY
Solvay TECHNYL® A 216 V15 Black 21N PA66, 15% glass fiber, Conditioned
Solvay TECHNYL A 205F PA66, DRY 美国苏威
18.TECHNYL PA66 A 216 S40:30%玻璃珠填料.
特点 表面光洁度好 低翘曲 良好的压缩强度
外貌 黑色 本色
处理方法 注塑成型
19.TECHNYL PA66 A 216 V10:10%玻璃纤维增强，注射成型。
添加剂 润滑剂
特点 润滑
用途 汽车应用 建材 电源/其它工具
外貌 黑色 可选颜色 本色
处理方法 注塑成型
20.TECHNYL PA66 A 216 V15:15％的玻璃纤维增强，注射成型
添加剂 润滑剂
特点 润滑
用途 汽车应用 建材 电源/其它工具
外貌 黑色 可选颜色 灰色 本色
处理方法 注塑成型
21.TECHNYL PA66 A 216 V20:20％的玻璃纤维增强，注射成型
添加剂 润滑剂
特点 润滑
用途 汽车应用 建材 电源/其它工具
外貌 黑色 可选颜色 本色
处理方法 注塑成型
22.TECHNYL PA66 A 216 V30:30％的玻璃纤维增强，注射成型
添加剂 润滑剂
特点 润滑
用途 汽车应用 建材 电源/其它工具
外貌 黑色 可选颜色 本色
处理方法 注塑成型
23.TECHNYL PA66 A 216 V35:聚酰胺尼龙66，35％的玻璃纤维增强，注射成型
添加剂 润滑剂
特点 润滑
用途 汽车应用 建材 电源/其它工具
外貌 黑色 可选颜色 本色
处理方法 注塑成型
Solvay TECHNYL A 205F PA66, DRY原厂原包，可提供原产地证明 、COA.COC.ROHS.MSDS.UL等资料。