LEXAN 沙伯基础创新 PC PC2200R 物性表
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.20 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) |
22 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) |
21.0 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动 |
|
|
内部方法 |
| --1 |
0.50 到 0.70 |
% |
内部方法 |
| 3.20 mm |
0.50 到 0.70 |
% |
内部方法 |
| 吸水率 |
|
|
|
| 饱和, 23°C |
0.35 |
% |
ISO 62 |
| 平衡, 23°C |
0.35 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 |
|
|
|
| R 级 |
120 |
|
ASTM D785 |
| R 计秤 |
120 |
|
ISO 2039-2 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| --2 |
2350 |
MPa |
ASTM D638 |
| -- |
2350 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服3 |
63.0 |
MPa |
ASTM D638 |
| 屈服 |
63.0 |
MPa |
ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服4 |
6.0 |
% |
ASTM D638 |
| 屈服 |
6.0 |
% |
ISO 527-2/50 |
| 断裂5 |
70 |
% |
ASTM D638 |
| 断裂 |
70 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距6 |
2300 |
MPa |
ASTM D790 |
| --7 |
2300 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| -- |
90.0 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距8 |
90.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C |
640 |
J/m |
ASTM D256 |
| -30°C9 |
12 |
kJ/m2 |
ISO 180/1A |
| 23°C10 |
65 |
kJ/m2 |
ISO 180/1A |
| 无缺口悬臂梁冲击 |
|
|
|
| 23°C |
无断裂 |
|
ASTM D4812, ISO 180/1U |
| -30°C11 |
无断裂 |
|
ISO 180/1U |
| 装有测量仪表的落镖冲击(23°C, Energy at Peak Load) |
55.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm |
133 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距12 |
133 |
°C |
ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm |
122 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距13 |
122 |
°C |
ISO 75-2/Af |
| 维卡软化温度 |
140 |
°C |
ISO 306/B50, ASTM D152514 |
| Ball Pressure Test(125°C) |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 - 流动 |
|
|
|
| -40 到 95°C |
7.0E-5 |
cm/cm/°C |
ASTM E831 |
| 23 到 80°C |
7.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| 导热系数 |
0.20 |
W/m/K |
ASTM C177, ISO 8302 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 体积电阻率 |
1.0E+15 |
ohms·cm |
ASTM D257, IEC 60093 |
| 介电强度(1.60 mm) |
27 |
kV/mm |
ASTM D149, IEC 60243-1 |
| 介电常数 |
|
|
ASTM D150, IEC 60250 |
| 60 Hz |
3.00 |
|
ASTM D150, IEC 60250 |
| 1 MHz |
3.00 |
|
ASTM D150, IEC 60250 |
| 耗散因数 |
|
|
ASTM D150, IEC 60250 |
| 60 Hz |
1.0E-3 |
|
ASTM D150, IEC 60250 |
| 1 MHz |
0.010 |
|
ASTM D150, IEC 60250 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级(1.60 mm) |
V-2 |
|
UL 94 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 折射率 |
1.586 |
|
ASTM D542, ISO 489 |
| 透射率(2540 μm) |
88.0 到 90.0 |
% |
ASTM D1003 |
| 雾度(2540 μm) |
0.80 |
% |
ASTM D1003
|