苏州海财塑化有限公司
LNP™ LUBRICOMP™ KP004AH compound
聚甲醛（POM）均聚物
SABIC Innovative Plastics
产品说明:
LNP LUBRICOMP KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant
Also known as: LNP* LUBRICOMP* Compound KL-4540 D HC
Product reorder name: KP004AH
| 添加剂 |
PTFE+硅酮润滑剂 (20%) |
|||||
| 特性 |
|
|||||
| 加工方法 |
注射成型 |
|||||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
|||
| 密度 |
1.49 |
g/cm3 |
ISO 1183, ASTM D792 |
|||
| 收缩率 |
|
|
|
|||
| 流动 : 24小时 |
2.1 |
% |
ASTM D955 |
|||
| 横向流动 : 24小时 |
2.1 |
% |
ASTM D955 |
|||
| 横向流量 : 24小时 |
2.1 |
% |
ISO 294-4 |
|||
| 流量 : 24小时 |
2.1 |
% |
ISO 294-4 |
|||
| 吸水率 (24 hr, 50% RH) |
0.20 |
% |
ASTM D570 |
|||
| 机械性能 |
额定值 |
单位制 |
测试方法 |
||
| 拉伸模量 |
|
|
|
||
| -- 2 |
2210 |
MPa |
ASTM D638 |
||
| -- |
2600 |
MPa |
ISO 527-2/1 |
||
| 抗张强度 |
|
|
|
||
| 断裂 |
50.3 |
MPa |
ASTM D638 |
||
| 断裂 |
45.0 |
MPa |
ISO 527-2 |
||
| 伸长率 |
|
|
|
||
| 断裂 |
13 |
% |
ASTM D638 |
||
| 断裂 |
11 |
% |
ISO 527-2 |
||
| 弯曲模量 |
|
|
|
||
| -- |
2410 |
MPa |
ASTM D790 |
||
| -- |
2800 |
MPa |
ISO 178 |
||
| 弯曲强度 |
|
|
|
||
| -- |
75.8 |
MPa |
ASTM D790 |
||
| -- |
77.0 |
MPa |
ISO 178 |
||
| 摩擦系数 |
|
|
ASTM D3702 Modified |
||
| Dynamic |
0.25 |
|
|
||
| Static |
0.16 |
|
|
||
| 磨损因数 - Washer |
9.00 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
||
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
||
| 悬壁梁缺口冲击强度 |
|
|
|
||
| 23°C |
48 |
J/m |
ASTM D256 |
||
| 23°C 3 |
4.5 |
kJ/m2 |
ISO 180/1A |
||
| 无缺口悬臂梁冲击 |
|
|
|
||
| 23°C |
430 |
J/m |
ASTM D4812 |
||
| 23°C 3 |
30 |
kJ/m2 |
ISO 180/1U |
||
| 装有测量仪表的落镖冲击 |
|
|
|
||
| 23°C, Energy at Peak Load |
5.00 |
J |
ASTM D3763 |
||
| -- |
1.00 |
J |
ISO 6603-2 |
||
| 热性能 |
额定值 |
单位制 |
测试方法 |
||
| 载荷下热变形温度 |
|
|
|
||
| 0.45 MPa, 未退火, 3.20 mm |
163 |
°C |
ASTM D648 |
||
| 1.8 MPa, 未退火, 3.20 mm |
99.4 |
°C |
ASTM D648 |
||
LNP? LUBRICOMP? POM KL005 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KN001 沙伯基础 compound SABIC Innovative Plastics Europe 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KP002 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KP003AXZ 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）均聚物
LNP? LUBRICOMP? POM KP004 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KP004A 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）均聚物
LNP? LUBRICOMP? POM KP004AH 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）均聚物
LNP? LUBRICOMP? POM KP004AXP 沙伯基础 compound SABIC Innovative Plastics Europe 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KP004AXZ 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）均聚物
LNP? LUBRICOMP? POM KP004L 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KP004XXP 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRICOMP? POM KZL16 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRILOY? POM K2000 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
LNP? LUBRILOY? POM K2000XXH 沙伯基础 compound SABIC Innovative Plastics 聚甲醛（POM）共聚物
供应:聚甲醛POM,防静电POM,导电POM,玻纤增强POM,抗紫外线耐候级POM,加铁氟龙POM,矿纤增强POM,碳纤增强POM,高粘度POM,高滑动POM,低粘度POM,食品级POM,低翘曲尺寸稳定POM,超高韧性POM,通用级POM,耐磨级POM,高抗冲POM,挤出级POM.
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
QQ:2290759979
邮箱:rzn8866@163.com
工程塑料：PEEK,PA46,ASA,PBT,POM,PC,PC+ABS,ASA+PC,PA6,PA66,PA46,PA11,PA12,PA6T,PA9T,PA612,PA1010.
PC/PBT，PC/PET，PC/PSU,PET，PMMA，PPA，PPE，PPO，ASA等
热弹性体：TPX,EVA,EMA，CPE，POE，PBE，POP，TPE，TPEE，TPO，TPR，TPU，TPV等
通用塑料：ABS，AS(SAS)，EAA，GPPS，HDPE，HIPS，LDPE，LLDPE，MBS，PP，PVC等
特种塑料:PTFE，PVDF，PFA，ETFE，PCTFE，PEEK，PEI，PPS，COC，LCP等