LubriOne™ ATH-000/04S NATURAL
聚甲醛(POM)均聚物
PolyOne Corporation
产品说明:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
供货地区 |
|
|||||
特性 |
|
|||||
用途 |
|
|||||
RoHS 合规性 |
RoHS 合规 |
|||||
形式 |
粒子 |
|||||
物理性能 |
额定值 |
单位制 |
测试方法 |
|||
比重 |
1.38 |
g/cm3 |
ASTM D792 |
|||
收缩率 |
|
|
ASTM D955 |
|||
流动 |
2.0 到 4.0 |
% |
|
|||
横向流动 |
1.0 到 3.0 |
% |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
||
拉伸模量 2 |
1930 |
MPa |
ASTM D638 |
||
抗张强度 2 |
|
|
ASTM D638 |
||
屈服 |
50.3 |
MPa |
|
||
断裂 |
50.3 |
MPa |
|
||
弯曲模量 3 |
2270 |
MPa |
ASTM D790 |
||
弯曲强度 3 |
75.8 |
MPa |
ASTM D790 |
||
摩擦系数 |
|
|
ASTM D1894 |
||
与钢 - 动态 |
0.11 |
|
|
||
与钢 - 静态 |
0.15 |
|
|
||
冲击性能 |
额定值 |
单位制 |
测试方法 |
||
悬壁梁缺口冲击强度 (23°C, 6.35 mm, 注塑) |
60 |
J/m |
ASTM D256A |
||
热性能 |
额定值 |
单位制 |
测试方法 |
||
载荷下热变形温度 |
|
|
ASTM D648 |
||
0.45 MPa, 未退火 |
158 |
°C |
|
||
1.8 MPa, 未退火 |
86.7 |
°C |
|
|
如未找到您合适的型号,或者有工程技术方面的疑问,欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
Q Q:2290759979
邮箱:rzn8866@163.com
Electrafil? POM J-80/CF/10/Natl 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM J-80/CF/20 NAT 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM 04008 mb 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM C BK 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM CF15 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM CO 13013 BK 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM CO AS 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物
Electrafil? POM CO 塑胶原料 Techmer Engineered Solutions 聚甲醛(POM)共聚物