LubriOne™ AT-000/05T 2S
聚甲醛（POM）共聚物
PolyOne Corporation
产品说明:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
| 供货地区 |
|
|||||
| 特性 |
|
|||||
| 用途 |
|
|||||
| RoHS 合规性 |
RoHS 合规 |
|||||
| 形式 |
粒子 |
|||||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
|||
| 比重 |
1.44 |
g/cm3 |
ASTM D792 |
|||
| 收缩率 - 流动 |
2.0 到 2.5 |
% |
ASTM D955 |
|||
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 3 |
586 |
MPa |
ASTM D638 |
| 抗张强度 3 (屈服) |
48.3 |
MPa |
ASTM D638 |
| 伸长率 3 (断裂) |
25 到 30 |
% |
ASTM D638 |
| 弯曲模量 |
1900 |
MPa |
ASTM D790 |
| 弯曲强度 |
75.8 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 (23°C, 3.18 mm, 注塑) |
69 |
J/m |
ASTM D256A |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火, 6.35 mm |
153 |
°C |
|
| 1.8 MPa, 未退火, 6.35 mm |
88.9 |
°C |
|
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+14 |
ohms |
ASTM D257 |
| 体积电阻率 |
1.0E+14 |
ohms·cm |
ASTM D257 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
HB |
|
UL 94 |
|
|
|||
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
Q Q:2290759979
邮箱:rzn8866@163.com
DynaMix? 塑胶原料 POM 1804-BLK Polymer Dynamix 聚甲醛（POM）共聚物
DynaMix? 塑胶原料 POM 1830MBH Polymer Dynamix 聚甲醛（POM）均聚物
DynaMix? 塑胶原料 POM 1844-15 GF Polymer Dynamix 聚甲醛（POM）共聚物
DynaMix? 塑胶原料 POM 625A Polymer Dynamix 聚甲醛 (POM) 共聚物合金
DynaMix? 塑胶原料 POM PD1801-BLK Polymer Dynamix 聚甲醛（POM）共聚物
DynaMix? 塑胶原料 POM PD1804-BLK Polymer Dynamix 聚甲醛（POM）共聚物
DynaMix? 塑胶原料 POM PD2003A Polymer Dynamix 聚甲醛（POM）共聚物