Hostaform® S 27063
聚甲醛（POM）共聚物
Celanese Corporation
产品说明:
Chemical abbreviation according to ISO 1043-1: POM-HI,
Molding compound ISO 9988- POM-K, M-GNPR, 05-001
POM copolymer, modified
Easy flowing elastomer-containing injection molding type based on
HOSTAFORM C 27021; with higher impact strength and slightly lower
hardness, rigidity and chemical resistance than the basic type; high
resistance to thermal and oxidative degradation.
UL-registration in natural and a thickness more than 1.57 mm as UL
94 HB.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm thickness.
Ranges of applications: For thin-walled molded parts with higher
energy-absorbing capacity
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
| 供货地区 |
|
|||||
| 特性 |
|
|||||
| 用途 |
薄壁部件 |
|||||
| RoHS 合规性 |
联系制造商 |
|||||
| 加工方法 |
注射成型 |
|||||
| 多点数据 |
Shear Stress vs. Shear Rate (ISO 11403-1) |
|||||
| 树脂ID (ISO 1043) |
POM-HI |
|||||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
|||
| 密度 |
1.39 |
g/cm3 |
ISO 1183 |
|||
| 溶化体积流率（MVR） (190°C/2.16 kg) |
20.0 |
cm3/10min |
ISO 1133 |
|||
| 收缩率 |
|
|
ISO 294-4 |
|||
| 横向流量 |
1.8 |
% |
|
|||
| 流量 |
1.9 |
% |
|
|||
| 吸水率 (饱和, 23°C) |
0.65 |
% |
ISO 62 |
|||
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
2200 |
MPa |
ISO 527-2/1A/1 |
| 拉伸应力 (屈服) |
54.0 |
MPa |
ISO 527-2/1A/50 |
| 拉伸应变 (屈服) |
9.0 |
% |
ISO 527-2/1A/50 |
| 标称拉伸断裂应变 |
30 |
% |
ISO 527-2/1A/50 |
| 拉伸蠕变模量 |
|
|
ISO 899-1 |
| 1 hr |
1850 |
MPa |
|
| 1000 hr |
1050 |
MPa |
|
| 弯曲模量 (23°C) |
2100 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
| -30°C |
6.0 |
kJ/m2 |
|
| 23°C |
9.0 |
kJ/m2 |
|
| 简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
| -30°C |
90 |
kJ/m2 |
|
| 23°C |
140 |
kJ/m2 |
|
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度 (1.8 MPa, 未退火) |
84.0 |
°C |
ISO 75-2/A |
| 熔融温度 3 |
166 |
°C |
ISO 11357-3 |
| 线形热膨胀系数 - 流动 |
1.2E-4 |
cm/cm/°C |
ISO 11359-2 |
|
|
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
Q Q:2290759979
邮箱:rzn8866@163.com
Delta POM ATL C27 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C27-UV 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9CL 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9-SG 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9-U6 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL H5 塑胶原料 Delta Polymers 聚甲醛（POM）均聚物
Delta POM ATL-1TFP40 塑胶原料 Delta Polymers 聚甲醛（POM）均聚物
Delta POM ATL-2PT20 -UV 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物