Hostaform® MT8U05
聚甲醛(POM)共聚物
Celanese Corporation
产品说明:
Hostaform® acetal copolymer grade MT8U05 is a special grade developed for medical industry applications containing low residual monomers and no animal products. The material can be identified by UV detectors. Hostaform® MT8U05 is an injection molding grade with a molecular weight for excellent moldability and optimum properties in demanding applications.
特性 |
|
|||||
用途 |
医疗/护理用品 |
|||||
RoHS 合规性 |
联系制造商 |
|||||
加工方法 |
注射成型 |
|||||
物理性能 |
额定值 |
单位制 |
测试方法 |
|||
密度 |
1.41 |
g/cm3 |
ISO 1183 |
|||
溶化体积流率(MVR) (190°C/2.16 kg) |
8.00 |
cm3/10min |
ISO 1133 |
|||
收缩率 |
|
|
ISO 294-4 |
|||
横向流量 |
1.8 |
% |
|
|||
流量 |
2.0 |
% |
|
|||
吸水率 (饱和, 23°C) |
0.65 |
% |
ISO 62 |
机械性能 |
额定值 |
单位制 |
测试方法 |
拉伸模量 |
2850 |
MPa |
ISO 527-2/1A/1 |
拉伸应力 (屈服) |
64.0 |
MPa |
ISO 527-2/1A/50 |
拉伸应变 (屈服) |
9.0 |
% |
ISO 527-2/1A/50 |
标称拉伸断裂应变 |
30 |
% |
ISO 527-2/1A/50 |
拉伸蠕变模量 |
|
|
ISO 899-1 |
1 hr |
2500 |
MPa |
|
1000 hr |
1300 |
MPa |
|
弯曲模量 (23°C) |
2700 |
MPa |
ISO 178 |
冲击性能 |
额定值 |
单位制 |
测试方法 |
简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
-30°C |
6.0 |
kJ/m2 |
|
23°C |
6.5 |
kJ/m2 |
|
简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
-30°C |
160 |
kJ/m2 |
|
23°C |
180 |
kJ/m2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
热变形温度 (1.8 MPa, 未退火) |
104 |
°C |
ISO 75-2/A |
熔融温度 2 |
166 |
°C |
ISO 11357-3 |
线形热膨胀系数 - 流动 |
1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
|
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
Q Q:2290759979
邮箱:rzn8866@163.com
Delta POM ATL C27 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL C27-UV 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL C9 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL C9CL 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL C9-SG 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL C9-U6 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物
Delta POM ATL H5 塑胶原料 Delta Polymers 聚甲醛(POM)均聚物
Delta POM ATL-1TFP40 塑胶原料 Delta Polymers 聚甲醛(POM)均聚物
Delta POM ATL-2PT20 -UV 塑胶原料 Delta Polymers 聚甲醛(POM)共聚物