聚甲醛（POM）共聚物
Celanese Corporation
产品说明:
Polyacetal copolymer, reduced emission
Easy flowing Injection molding type like C 13021 XAP, but with higher
strength, rigidity and hardness over the entire permissible
temperature range for HOSTAFORM; good chemical resistance to
solvents, fuel and strong alkalis as well as good hydrolysis
resistance; high resistance to thermal and oxidative degradation.
Emissions according to VDA 275 < 10 ppm (natural and colored grades)
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: For molded parts with higher requirements to
strength, rigidity und hardness, ranges of applications with fuel
contact.
| 供货地区 |
|
|||||
| 特性 |
|
|||||
| 机构评级 |
|
|||||
| RoHS 合规性 |
· 联系制造商 |
|||||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
|||
| 密度 |
1.41 |
g/cm3 |
ISO 1183 |
|||
| 溶化体积流率（MVR） (190°C/2.16 kg) |
12.0 |
cm3/10min |
ISO 1133 |
|||
| 收缩率 |
|
|
ISO 294-4 |
|||
| 横向流量 |
1.8 |
% |
|
|||
| 流量 |
2.0 |
% |
|
|||
| 吸水率 (饱和, 23°C) |
0.65 |
% |
ISO 62 |
|||
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
3050 |
MPa |
ISO 527-2/1A/1 |
| 拉伸应力 (屈服) |
68.0 |
MPa |
ISO 527-2/1A/50 |
| 拉伸应变 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
| 标称拉伸断裂应变 |
20 |
% |
ISO 527-2/1A/50 |
| 拉伸蠕变模量 |
|
|
ISO 899-1 |
| 1 hr |
2750 |
MPa |
|
| 1000 hr |
1450 |
MPa |
|
| 弯曲模量 (23°C) |
3000 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
| -30°C |
6.0 |
kJ/m2 |
|
| 23°C |
6.7 |
kJ/m2 |
|
| 简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
| -30°C |
120 |
kJ/m2 |
|
| 23°C |
120 |
kJ/m2 |
|
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度 (1.8 MPa, 未退火) |
107 |
°C |
ISO 75-2/A |
| 熔融温度 2 |
170 |
°C |
ISO 11357-3 |
| 线形热膨胀系数 - 流动 |
1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+14 |
ohms |
IEC 60093 |
| 体积电阻率 |
1.0E+14 |
ohms·cm |
IEC 60093 |
| 介电强度 |
35 |
kV/mm |
IEC 60243-1 |
| 相对电容率 |
|
|
IEC 60250 |
| 100 Hz |
4.00 |
|
|
| 1 MHz |
4.00 |
|
|
| 耗散因数 |
|
|
IEC 60250 |
| 100 Hz |
2.0E-3 |
|
|
| 1 MHz |
5.0E-3 |
|
|
| 漏电起痕指数 |
600 |
V |
IEC 60112 |
苏州润之来塑化有限公司
手机:1 8 0 1 5 4 9 5 9 1 9
电话:0512-53128920
传真:0512-53128921
Q Q:2290759979
邮箱:rzn8866@163.com
Delta POM ATL C27 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C27-UV 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9CL 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9-SG 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL C9-U6 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物
Delta POM ATL H5 塑胶原料 Delta Polymers 聚甲醛（POM）均聚物
Delta POM ATL-1TFP40 塑胶原料 Delta Polymers 聚甲醛（POM）均聚物
Delta POM ATL-2PT20 -UV 塑胶原料 Delta Polymers 聚甲醛（POM）共聚物