东莞市崀峰塑胶原料有限公司
Hostaform? LX90GC15
Acetal (POM) Copolymer
Celanese Corporation
15% 玻璃纤维增强材料
产品说明：
Preliminary Data Sheet
Hostaform? LX90GC15 is a specialty metallic appearance acetal copolymer grade that is integrally colored and has a nominal 15% fiber glass loading. This grade provides additional strength and stiffness over unfilled acetal grades while presenting a metal appearance surface.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
Hostaform? LX90GC15 is a specialty metallic appearance acetal copolymer grade that is integrally colored and has a nominal 15% fiber glass loading. This grade provides additional strength and stiffness over unfilled acetal grades while presenting a metal appearance surface.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
Chemical abbreviation according to ISO 1043-1: POM
填料/增强材料
|
|
| 特性 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.50 | g/cm3 | ISO 1183 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.2 | % | ISO 294-4 |
| 流动方向 | 0.70 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 0.85 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 5500 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (断裂) | 75.0 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 4.0 | % | ISO 527-2/1A/5 |
| 弯曲模量 (23°C) | 5200 | MPa | ISO 178 |