ExxonMobil Escorene LD 319.92 Film
escorene超LD 319.92为9重量%的醋酸乙烯酯共聚物膜树脂,具有优异的抗冲击强度和热封性能
Physical Properties |
Metric |
English |
Comments |
Density |
0.930 g/cc |
0.0336 lb/in3 |
ExxonMobil Method |
Vinyl Acetate Content |
9.0 % |
9.0 % |
ExxonMobil Method |
Melt Flow |
2.0 g/10 min |
2.0 g/10 min |
ExxonMobil Method |
|
Mechanical Properties |
Metric |
English |
Comments |
Film Tensile Strength at Yield, MD |
6.89 MPa |
1000 psi |
at 2% offset; ASTM D882 |
Film Tensile Strength at Yield, TD |
6.27 MPa |
910 psi |
at 2% offset; ASTM D882 |
Film Elongation at Break, MD |
330 % |
330 % |
ASTM D882 |
Film Elongation at Break, TD |
660 % |
660 % |
ASTM D882 |
Film Elongation at Yield, MD |
7.9 % |
7.9 % |
ASTM D882 |
Film Elongation at Yield, TD |
6.4 % |
6.4 % |
ASTM D882 |
Elmendorf Tear Strength, MD |
3.15 g/micron |
80.0 g/mil |
ASTM D1922 |
Elmendorf Tear Strength, TD |
2.625 g/micron |
66.67 g/mil |
ASTM D1922 |
Dart Drop |
6.5618 g/micron |
166.67 g/mil |
ASTM D1709 |
Film Tensile Strength at Break, MD |
30.5 MPa |
4430 psi |
ASTM D882 |
Film Tensile Strength at Break, TD |
27.4 MPa |
3980 psi |
ASTM D882 |
1% Secant Modulus, MD |
106 MPa |
15400 psi |
ASTM D882 |
1% Secant Modulus, TD |
116 MPa |
16800 psi |
ASTM D882 |
|
Thermal Properties |
Metric |
English |
Comments |
Melting Point |
98.9 °C |
210 °F |
Peak Melting Temperature; ExxonMobil Method |
Crystallization Temperature |
85.0 °C |
185 °F |
ExxonMobil Method |
Vicat Softening Point |
80.6 °C |
177 °F |
ASTM D1525 |
|
Optical Properties |
Metric |
English |
Comments |
Haze |
1.5 % |
1.5 % |
ASTM D1003 |
Gloss |
88 % |
88 % |
45°; ASTM D2457 |
|
|
|
|