ExxonMobil Exceed 2718CB Premium

超过2718cb树脂是一种己烯共聚物使用埃克森美孚化工EXXPOL®技术生产。由树脂薄膜2718cb优异的拉伸性能和冲击韧性和穿刺。这些优异的性能，以及优良的性能，使这一为单层和多层流延膜的通用型树脂。

Availability: Europe, Latin America, North America and South America

可用性：欧洲，拉丁美洲的美国，北美国和南美国

Additive:

添加剂：

Antiblock: No

防：没有

Slip: No

滑：无

Processing Aid: No

加工助剂：无

Thermal Stabilizer: Yes

热稳定剂：是的

Applications:

应用：

Bag in Box

盒中袋

Barrier Food Packaging

阻隔食品包装

Blown Film

吹塑薄膜

Cast Film

电影演员

Cast Stretch Film

流延膜

Diaper Backsheet

尿布的底片

Form Fill and Seal Packaging

填充和密封包装

Physical Properties Metric English Comments Density  0.918 g/cc 0.0332 lb/in3 ASTM D1505 Thickness  20.3 microns 0.800 mil Melt Flow  2.7 g/10 min 2.7 g/10 min ASTM D1238   Mechanical Properties Metric English Comments Film Tensile Strength at Yield, MD  8.55 MPa 1240 psi at 2% offset; ASTM D882 Film Tensile Strength at Yield, TD  7.86 MPa 1140 psi at 2% offset; ASTM D882 Film Elongation at Break, MD  470 % 470 % ASTM D882 Film Elongation at Break, TD  720 % 720 % ASTM D882 Puncture Energy  4.18 J 3.08 ft-lb Exxon Mobil Method Elmendorf Tear Strength MD  170 g 170 g ASTM D1922 Elmendorf Tear Strength TD  420 g 420 g ASTM D1922 Elmendorf Tear Strength, MD  8.366 g/micron 212.5 g/mil ASTM D1922 Elmendorf Tear Strength, TD  20.7 g/micron 525 g/mil ASTM D1922 Dart Drop  8.366 g/micron 212.5 g/mil ASTM D1709 Dart Drop Test  170 g 0.375 lb ASTM D1709 Film Tensile Strength at Break, MD  75.08 MPa 10890 psi ASTM D882 Film Tensile Strength at Break, TD  51.4 MPa 7450 psi ASTM D882 1% Secant Modulus, MD  109 MPa 15800 psi ASTM D882 1% Secant Modulus, TD  132 MPa 19100 psi ASTM D882   Thermal Properties Metric English Comments Melting Point  117 °C 243 °F Peak Melting Temperature; ExxonMobil Method   Optical Properties Metric English Comments Haze  1.8 % 1.8 % ASTM D1003 Gloss  东莞市艾博（国际）塑胶进口出口有限公司系列产品可随货提供原材料物性，原材料产地证明SGS.MSDS.UL黄卡等相关详细资料，可开具17%增值税发票.公司秉着“以诚为本，以信为用”的经营理念。与客户是建立在互惠、互利、互信的基础上长期合作。共创双赢局面，愿与各界人士真诚合作，共同发展，携手共创辉煌的明天.