ExxonMobil LD 146.NH Cast|价格|厂家|多少钱-全球塑胶网-移动端

艾博（国际）塑胶进出口有限公司现货供应 ExxonMobil LD 146.NH Cast ，原产原包，可随货提供原材料物性，COA,SGS.MSDS.UL黄卡等相关详细资料，欢迎来人来电咨讯

ExxonMobil LD 146.NH Cast

LD 146.nh是均聚物膜树脂提供良好的透明度，韧性和刚度。这是用在食品包装复合膜

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in3	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	3.75 g/10 min	3.75 g/10 min	ExxonMobil Method
Antiblock Level	1200 ppm	1200 ppm
Slip Level	900 ppm	900 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.38 MPa	1360 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	9.58 MPa	1390 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	200 %	200 %	ASTM D882
Film Elongation at Break, TD	560 %	560 %	ASTM D882
Film Elongation at Yield, MD	6.4 %	6.4 %	ASTM D882
Film Elongation at Yield, TD	5.5 %	5.5 %	ASTM D882
Elmendorf Tear Strength MD	260 g	260 g	ASTM D1922
Elmendorf Tear Strength TD	140 g	140 g	ASTM D1922
Elmendorf Tear Strength, MD	6.823 g/micron	173.3 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	3.67 g/micron	93.3 g/mil	ASTM D1922
Dart Drop	2.36 g/micron	60.0 g/mil	ASTM D1709
Dart Drop Test	90.0 g	0.198 lb	ASTM D1709
Film Tensile Strength at Break, MD	21.2 MPa	3080 psi	ASTM D882
Film Tensile Strength at Break, TD	18.3 MPa	2650 psi	ASTM D882
1% Secant Modulus, MD	176 MPa	25500 psi	ASTM D882
1% Secant Modulus, TD	212 MPa	30800 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	108 °C	226 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	95.0 °C	203 °F	ExxonMobil Method
Vicat Softening Point	91.7 °C	197 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	5.5 %	5.5 %	ASTM D1003
Gloss	73 %	73 %	45°; ASTM D2457