ExxonMobil LD 117.08 Blown
LD 117树脂是均聚物薄膜的树脂具有良好的透明度和良好的刚度。从LD 117树脂膜可用于包装应用的推动型的包装设备。电影由LD 117树脂可以提取到1百万计
Physical Properties |
Metric |
English |
Comments |
Density |
0.929 g/cc |
0.0336 lb/in3 |
ExxonMobil Method |
Thickness |
38.1 microns |
1.50 mil |
|
Melt Flow |
1.6 g/10 min |
1.6 g/10 min |
ExxonMobil Method |
|
Mechanical Properties |
Metric |
English |
Comments |
Film Tensile Strength at Yield, MD |
13.3 MPa |
1930 psi |
at 2% offset; ASTM D882 |
Film Tensile Strength at Yield, TD |
15.0 MPa |
2170 psi |
at 2% offset; ASTM D882 |
Film Elongation at Break, MD |
170 % |
170 % |
ASTM D882 |
Film Elongation at Break, TD |
550 % |
550 % |
ASTM D882 |
Film Elongation at Yield, MD |
5.6 % |
5.6 % |
ASTM D882 |
Film Elongation at Yield, TD |
5.0 % |
5.0 % |
ASTM D882 |
Elmendorf Tear Strength MD |
250 g |
250 g |
ASTM D1922 |
Elmendorf Tear Strength TD |
200 g |
200 g |
ASTM D1922 |
Elmendorf Tear Strength, MD |
6.559 g/micron |
166.6 g/mil |
ASTM D1922 |
Elmendorf Tear Strength, TD |
5.248 g/micron |
133.3 g/mil |
ASTM D1922 |
Dart Drop |
2.10 g/micron |
53.3 g/mil |
ASTM D1709 |
Dart Drop Test |
80.0 g |
0.176 lb |
ASTM D1709 |
Film Tensile Strength at Break, MD |
25.0 MPa |
3630 psi |
ASTM D882 |
Film Tensile Strength at Break, TD |
20.3 MPa |
2940 psi |
ASTM D882 |
1% Secant Modulus, MD |
304 MPa |
44100 psi |
ASTM D882 |
1% Secant Modulus, TD |
359 MPa |
52000 psi |
ASTM D882 |
|
Thermal Properties |
Metric |
English |
Comments |
Melting Point |
114 °C |
238 °F |
Peak Melting Temperature; ExxonMobil Method |
Crystallization Temperature |
103 °C |
217 °F |
ExxonMobil Method |
Vicat Softening Point |
105 °C |
221 °F |
ASTM D1525 |
|
Optical Properties |
Metric |
English |
Comments |
Haze |
6.5 % |
6.5 % |
ASTM D1003 |
Gloss |
70 % |
70 % |
45°; ASTM D2457 |
|
|
|
|
|
|