ExxonMobil LD 334.82 Clear
LD 334树脂生产具有优异的冲击强度的薄膜，良好的热封性能，低温性能
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 4.2 % | 4.2 % | ExxonMobil Method |
| Melt Flow | 1.25 g/10 min | 1.25 g/10 min | ExxonMobil Method |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Slip Level | 800 ppm | 800 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.07 MPa | 1170 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.65 MPa | 1110 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 |
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 |
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 |
| Dart Drop Test | 180 g | 0.397 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.3 MPa | 3530 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.2 MPa | 3360 psi | ASTM D882 |
| 1% Secant Modulus, MD | 141 MPa | 20400 psi | ASTM D882 |
| 1% Secant Modulus, TD | 163 MPa | 23700 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 220 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 91.0 °C | 196 °F | ExxonMobil Method |
| Vicat Softening Point | 87.2 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.4 % | 7.4 % | ASTM D1003 |
| Gloss | 68 % | 68 % | 45°; ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
|
|||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
|---|